Products
SUMMARY
- ST510S-D-AR is applicable in high temperature system.
- ST510S-D-AR is suitable for dry mixed and has no special requirement on the quality of mixing water.
- ST510S-D-AR has good top strength when used in long formation sealant of well cementation.
- ST510S-D-AR is not easy to damp and cake and has long expiration period.
SPECIAL ATTENTIONS
- ST510S-D-AR may influence the top strength of the set cement when the curing temperature is lower than the bottom hole cycle temperature.
PHYSICAL AND CHEMICAL INDICATORS
Appearance |
Bulk Density g/cm3 |
Water-Solubility |
0.315mm Sieve (45 mesh) Residues % |
gray powder |
1.20±0.10 |
partly |
<12 |
CEMENT SLURRY PERFORMANCE
Item |
Test Condition |
Technical Indicator |
Initial consistency, Bc |
120℃/61min, 73.9MPa |
≤30 |
40-100Bc thickening time, min |
≤40 |
|
Thickening time adjustability |
Adjustable |
|
Thickening curve |
Normal |
|
Free fluid , % |
≤1.4 |
|
24h compressive strength, MPa |
120℃, 20.7MPa |
≥14 |
Composition: API Class G(HSR) 600g;silica flour 210g(35%);silica fume 36g(6%);mixed water 342g;defoamer 1.8g(0.3%); ST510S-D-AR. |
||
Remarks: the dosage of ST510S-D-AR is determined under the precondition of adjusting the thickening time range of cement slurry at 120℃ to 170—330 min. |
APPLICATIONS
Application temperature: generally194-302℉(90-150℃) (BHCT).
Dosage: ST510S-D-AR generally 1.0-4.0% (BWOC).
PACKING
ST510S-D-AR is packed with 25kg bag. It can also be packed according to user requirements.